Low Abrasion Activated Alumina Oxide Desiccant, Activated Alumina Oxide Ball

Model NO.
KA-401, KA-402, KA-403, KA-404, KA-405
Application
Adsorbent Air Separation Defluorinating Catalyst C
Al2O3 Content
93% Min
MOQ(Kg)
500
Delivery Time
Within One Week
Country of Origin
China
Who We Are
Manufacture
Established Time
2002
Certification
ISO9001:2015
Keywords
Activated Alumina
Trademark
XINTAO
Transport Package
25kg/Plastic Bag, Jumbo Bag, Steel Drum
Specification
1~2mm; 2~3mm; 3~5mm; 4~6mm; 6~8mm
Origin
China
HS Code
3824999990
The key to our success is "Good Product Excellent, Reasonable Rate and Efficient Service" for Low Abrasion Activated Alumina Oxide Desiccant, Activated Alumina Oxide Ball, The product will supply to all over the world, such as: Cambodia, Lisbon, Guatemala, During the 10 years of operating, our company always try our best to bring consumption satisfaction for user, built a brand name for ourselves and a solid position in the international market with major partners come from many countries such as Germany, Israel, Ukraine, United Kingdom, Italy, Argentina, France, Brazil, and so on. Last but not least, price of our products are very suitable and have fairly high competition with other companies.
Jiangxi Xintao Technology Co., Ltd. Diamond / Audited Supplier
Low Abrasion Activated Alumina Oxide Desiccant, Activated Alumina Oxide Ball

Product Introduction: 
Activated Alumina, there are many micro-pathsso the specific surface is large
Xintao Activated Alumina, the defluorinate effect is goodThe capacity is stableIt has high strengthlow
abrasionno soften in water, no expansion, no powdery no crackIt can widely used in the deep drying
of cracked gas, ethylene and propylene, hydrogen-generation, air separation, instrument air drying and
fluorine treatment for H2O2, also in the absorbing pollution material, such as H2S, SO2, HF and paraffin
in the waste gas, especially in the drinking water defluorinate. 
Typical Chemical Formula: Al2O3·nH2O (0≤n≤0.8)
Technical Parameter: 

Model Activated Alumina
Color White
Shape Sphere
Type KA401 KA402 KA403 KA404 KA405
Crystal Type X-p X-p Y Y X-p
Chemical Composition Al2O3 Content (%) ≥93 ≥93 ≥93 ≥93 ≥93
Na2O Content (%) ≤0.3 ≤0.3 ≤0.5 0.15-0.3 ≤0.3
Physical properties Bulk density (g/ml) 0.68-0.72 0.70-0.75 0.65-0.75 0.70-0.80 0.72-0.78
Pore volume (ml/g) 0.30-0.45 0.30-0.42 0.40-0.46 0.40 0.30-0.50
Surface area (m2/g) ≥300 ≥300 260-300 ≥300 ≥300
Active (%) / / 56-62 / /
Attrition loss (%) ≤1.0 ≤1.0 ≤1.0 ≤0.4 ≤0.8
LOI (%) ≤8 ≤8 ≤8 ≤5 ≤8
Static absorption (%)
(RH=60%)
Water
Absorption
Fluorine
Absorption
Water
Absorption
Water
Absorption
Water
Absorption
17-19 0.2-0.3 50 50-70 17-19
Crushing Strength (N/PC) Φ1-2 (mm) ≥40 ≥40 / / /
Φ2-3 (mm) ≥70 ≥70 / / /
Φ3-5 (mm) ≥120 / ≥120 ≥120 ≥120
Φ4-6 (mm) ≥150 / ≥150 ≥150 ≥150
Φ5-7 (mm) ≥200 / / / ≥200
Φ6-8 (mm) ≥300 / / / ≥300
Φ12-14 (mm) ≥350 / / / /